PP Rods | |||
---|---|---|---|
Diameter(mm) | Tolerance(mm) | Length(mm) | |
L1000 | L3000 | ||
15 | +0.1 ~ +1.0 | 1000 | 3000 |
20 | 1000 | 3000 | |
25 | 1000 | 3000 | |
30 | +0.2 ~ +1.5 | 1000 | 3000 |
35 | 1000 | 3000 | |
40 | +0.2 ~ +2.5 | 1000 | 3000 |
45 | 1000 | 3000 | |
50 | 1000 | 3000 | |
55 | 1000 | 3000 | |
60 | +0.5 ~ +3.0 | 1000 | 3000 |
65 | 1000 | 3000 | |
70 | 1000 | 3000 | |
75 | 1000 | 3000 | |
80 | 1000 | 3000 | |
85 | 1000 | 3000 | |
90 | +0.5 ~ +3.5 | 1000 | 3000 |
95 | 1000 | 3000 | |
100 | 1000 | 3000 | |
110 | 1000 | 3000 | |
120 | +1.0 ~ +4.5 | 1000 | 3000 |
130 | 1000 | 3000 | |
140 | 1000 | 3000 | |
150 | +1.5 ~ +6.0 | 1000 | 3000 |
160 | 1000 | 3000 | |
180 | 1000 | 3000 | |
200 | +2.0 ~ +7.0 | 1000 | 3000 |
210 | 1000 | 3000 | |
250 | 1000 | 3000 |
PP Board | |||
---|---|---|---|
Thickness(mm) | Tolerance(mm) | Specifications | |
1000 X 2000 | 1200 x 2400 | ||
3 | -0.2 ~ +0.3 | 1000 X 2000 | 1200 x 2400 |
4 | 1000 X 2000 | 1200 x 2400 | |
5 | 1000 X 2000 | 1200 x 2400 | |
6 | -0.3 ~ +0.4 | 1000 X 2000 | 1200 x 2400 |
8 | 1000 X 2000 | 1200 x 2400 | |
10 | 1000 X 2000 | 1200 x 2400 | |
12 | +0.1 ~ +1.5 | 1000 X 2000 | 1200 x 2400 |
15 | 1000 X 2000 | 1200 x 2400 | |
20 | +0.1 ~ +2.0 | 1000 X 2000 | 1200 x 2400 |
25 | 1000 X 2000 | 1200 x 2400 | |
30 | 1000 X 2000 | 1200 x 2400 | |
35 | +0.8 ~ +4.0 | 1000 X 2000 | 1200 x 2400 |
40 | 1000 X 2000 | 1200 x 2400 | |
45 | 1000 X 2000 | 1200 x 2400 | |
50 | +0.8 ~ +4.5 | 1000 X 2000 | 1200 x 2400 |
60 | 1000 X 2000 | 1200 x 2400 | |
70 | +1.0 ~ +8.0 | 1000 X 2000 | 1200 x 2400 |
80 | 1000 X 2000 | 1200 x 2400 | |
100 | 1000 X 2000 | 1200 x 2400 | |
110 | +1 ~ +4 | 1000 X 2000 | 1200 x 2400 |
120 | 1000 X 2000 | 1200 x 2400 | |
130 | 1000 X 2000 | 1200 x 2400 | |
140 | 1000 X 2000 | 1200 x 2400 | |
150 | 1000 X 2000 | 1200 x 2400 |
● Physical property
Varieties | PP | |||
---|---|---|---|---|
Items | Test Method | Unit | ||
specific gravity | D-792 | G/㎠ | 0.91 | |
Tensile strength | D-638 | MPa | 35 | |
Elongation | D-638 | % | 30 | |
Tensile Modulus | D-638 | MPa | 1177 | |
Compressive strength | Yield point | D-695 | MPa | - |
5%Transformation (10%Transformation) | D-695 | MPa | 49 | |
Flexural strength | D-790 | MPa | - | |
Flexural modulus | D-790 | MPa | - | |
IZOD Notched Impact value | D-256 | J/m{kgf•cm/ | 39 | |
Rockwell hardness | D-785 | R-Scale | 110 | |
Shorer hardness | D-785 | D type | 77 | |
Melting point | - | ℃ | 120 | |
Heat Deflection Temperature | 0.445MPa | D-648 | ℃ | 105 |
1.820MPa | D-648 | ℃ | 80 | |
Continuous use temperature | - | ℃ |
| |
Coefficient of Linear Thermal Expansion | D-696 | x105/℃ | 11 | |
Absorption(Underwater, Equilibrium) | D-570 | % | 0.01 | |
Volume resistivity | D-257 | Ω•m | > 1014 | |
Breakdown voltage | D-149 | Kv/mm | - | |
Combustibility | (UL94) | - | HB | |
Chemical resistance | Oil | - | △ |
|