Urethane (meth)acrylate

- Urethane oligomers are composed of various isocyanates and polyol compounds.

And urethane (meth)acrylates are manufactured by replacing the both ends of urethane oligomer to acrylic functional groups.

Therefore, the performance of urethane(meth)acrylate such as toughness, flexibility and hardness is affected by the composition of urethane oligomers.

Urethane (meth)acrylates are also widely used for hard coating and adhesive manufacturing.

Grade	Active Hydrogen species	Isocyanate	Viscosity(mPa·ｓ)	Functional Group No.	Molecular weight（Mw)	Characteristic	Remark
KUA-CA2I	2 functional mathacrylate	IPDI	1,200,000 ~ 1,600,000	2	1,500 ~ 2,500	High hardness Humidification
KUA-CB2I	2 functional mathacrylate	IPDI	2,000,000 ~ 3,000,000	2	3,000 ~ 5000	High hardness
KUA-PCA2I	2 functional mathacrylate	IPDI	2,000,000 ~ 3,000,000	2	3,000 ~ 5000	Heat resistance Weatherproof Water resistance
KUA-PCB-2I	2 functional mathacrylate	IPDI	5,500,000 ~ 6,500,000	2	6,000 ~ 10,000	Heat resistance Weatherproof Water resistance
KUA-PCC-2I	2 functional mathacrylate	IPDI	High viscosity	2	8,000 ~ 15,000	Heat resistance Weatherproof Water resistance
KUA-PCD2I	2 functional mathacrylate	IPDI	4,000,000 ~ 5,000,000	2	10,000 ~ 20,000	Heat resistance Weatherproof Water resistance	MEK 30% dilution
KUA-PEA2I	2 functional mathacrylate	IPDI	3,000,000 ~ 4,000,000	2	25,000 ~ 40,000	Flexibility / Adhesion
KUA-PEB2I	2 functional mathacrylate	IPDI	100,000 ~ 150,000	2	8,000 ~ 15,000	Flexibility / Adhesion
KUA-PEC2I	2 functional acrylic	IPDI	500,000 ~ 1,000,000	2	15,000 ~ 25,000	Flexibility / Adhesion
KUA-PED2I	2 functional mathacrylate	IPDI	700,000 ~ 1,000,000	2	4,000 ~ 9,000	Flexibility / Adhesion
KUA-PEE2I	2 functional mathacrylate	IPDI	150,000 ~ 350,000	2	10,000 ~ 20,000	Flexibility / Adhesion
KUA-PEF2I	2 functional mathacrylate	IPDI	110,000 ~ 120,000	2	2,000 ~ 5,000	Water resistance Flexibility Adhesion
KUA-PEA2T	2 functional acrylic	TDI	High viscosity	2	7,000 ~ 15,000	Water resistance Adhesion Stiffness	Diluted monomer IBX15％
KUA-PCD2I	2 functional mathacrylate	IPDI	High viscosity	2	7,000 ~ 15,000	Adhesion Stiffness	Diluted monomer IBX15％
KUA-PCD2I	2 functional mathacrylate	IPDI	High viscosity	2	7,000 ~ 15,000	Weatherproof Adhesion Stiffness	Diluted monomer IBX15％
KUA-2TM	Functional methacrylate	TMDI	3,000 ~ 8,000	2	400 ~ 600	Low viscosity	No after yellowing
KUA-4I	2 functional acrylic	IPDI	10,000 ~ 30,000	4	550 ~ 750	Low curl	No after yellowing
KUA-4H	2 functional acrylic	HDI	10,000 ~ 30,000	4	500 ~ 700	Low curl	No after yellowing
KUA-4T	2 functional acrylic	TDI	10,000 ~ 30,000	4	500 ~ 700	Low curl / High sensitivity
KUA-6I	3 functional acrylic	IPDI	10,000 ~ 40,000	6	800 ~ 1,000	High hardness	No after yellowing
KUA-6H	3 functional acrylic	HDI	10,000 ~ 40,000	6	800 ~ 1,000	High hardness Flexibility	No after yellowing
KUA-6T	3 functional acrylic	TDI	10,000 ~ 40,000	6	800 ~ 1,000	High crosslinking High hardness
KUA-10I	5 functional acrylic	IPDI	20,000 ~ 50,000	10	1,400 ~ 1,800	High hardness	No after yellowing
KUA-10H	5 functional acrylic	HDI	20,000 ~ 50,000	10	1,300 ~ 1,700	High hardness Flexibility	No after yellowing
KUA-10T	5 functional acrylic	TDI	20,000 ~ 50,000	10	1,300 ~ 1,700	High crosslinking High hardness
KUA-3N	Functional acrylic	Isocya nurate	20,000 ~ 50,000	3	1,800 ~ 2,200	Less shrinkage after crosslinking	No after yellowing
KUA-9N	3 functional acrylic	Isocya nurate	20,000 ~ 30,000	9	1,400 ~ 1,800	High hardness	No after yellowing
KUA-9NTF	3 functional acrylic	Isocya nurate	10,000 ~ 40,000	9	1,400 ~ 1,800	High hardness Tin free	No after yellowing
KUA-15N	5 functional acrylic	Isocya nurate	10,000 ~ 40,000	15	2,300 ~ 2,900	High hardness	No after yellowing